Compound for organic electronic element, organic electronic element using same and electronic device thereof

ABSTRACT

Provided is a novel mixture capable of improving luminous efficiency, stability, and lifespan of an element, an organic electric element using the same, and an electronic device therefor.

BACKGROUND Technical Field

The present invention relates to compound for organic electric element, organic electric element using the same, and an electronic device thereof.

Background Art

In general, organic light emitting phenomenon refers to a phenomenon that converts electric energy into light energy by using an organic material. An organic electric element using an organic light emitting phenomenon usually has a structure including an anode, a cathode, and an organic material layer interposed therebetween. Here, in order to increase the efficiency and stability of the organic electric element, the organic material layer is often composed of a multi-layered structure composed of different materials, and for example, may include a hole injection layer, a hole transport layer, an emitting layer, an electron transport layer, an electron injection layer and the like.

A material used as an organic material layer in an organic electric element may be classified into a light emitting material and a charge transport material, such as a hole injection material, a hole transport material, an electron transport material, an electron injection material and the like depending on its function.

Bis-type cyclic compounds including heteroatoms have a very large difference in properties depending on the material structure, and are therefore applied to various layers as materials for organic electric elements. In particular, the band gap (HOMO, LUMO), electrical properties, chemical properties, and physical properties are different depending on the number of rings and the fused position, and the type and arrangement of heteroatoms, therefore application development for layers of various organic electric elements using the same has been progressed. In a phosphorescent organic electric element using a phosphorescent dopant material, the LUMO and HOMO levels of the host material have a great influence on the efficiency and life span of the organic electric element, and depending on whether electron and hole injection in the emitting layer can be efficiently controlled, charge balance in the emitting layer, dopant quenching, and reduction in efficiency and lifespan due to light emission at the hole transport layer interface can be prevented.

For fluorescent and phosphorescent host materials, recently we have been studying the increase of efficiency and life span of organic electric elements using TADF (thermal activated delayed fluorescent), exciplex, etc., particularly, and many studies have been carried out to identify the energy transfer method from the host material to the dopant material.

Although there are various methods for identifying the energy transfer in the emitting layer for TADF (thermally activated delayed fluorescent) and exciplex, it can be easily confirmed by the PL lifetime (TRTP) measurement method.

The TRTP (Time Resolved Transient PL) measurement method is a method of observing a decay time after irradiating a pulsed light source onto a host thin film, and is a measurement method that can identify the energy transfer method by observing energy transfer and emission delay time. The TRTP measurement is a measurement method capable of distinguishing fluorescence and phosphorescence, and an energy transfer method in a mixed host material, an exciplex energy transfer method, and a TADF energy transfer method.

As such, there are various factors that affect the efficiency and lifespan depending on how energy is transferred from the host material to the dopant material.

Since the energy transfer method is different depending on the material, the development of a stable and efficient host material for an organic electric element has not been sufficiently performed. Therefore, development of new materials is continuously required, and especially development of a host material for an emitting layer is urgently required.

Reference KR101170666 B1 was used as a prior art document.

DETAILED DESCRIPTION OF THE INVENTION Summary

The present invention has been proposed in order to solve the problems of the phosphorescent host material, and an object of the present invention is, by controlling the HOMO level of a host material of a phosphorescent emitting organic electric element including a phosphorescent dopant, to provide a compound capable of controlling charge balance and of improving efficiency and lifespan in an emitting layer, and an organic electric element using the same and an electronic device thereof.

Technical Solution

In order to control the efficient hole injection in the emitting layer of the phosphorescent emitting organic electric element, by containing a second host material in combination with a first host material as a main component, the energy barrier between the emitting layer and the adjacent layer can be reduced, and the charge balance in the emitting layer is maximized to provide high efficiency and high lifespan of the organic electric element.

The present invention provides an organic electronic element comprising a first electrode, a second electrode, and an organic material layer formed between the first electrode and the second electrode, wherein the organic material layer comprises an emitting layer, wherein the emitting layer is a phosphorescent emitting layer and comprises a first host compound represented by Formula 1 and a second host compound represented by Formula 2.

In Formula 1, M is represented by a C₆-C₆₀ arylene group or Formula 1-1.

The present invention also provides organic electric elements and electronic devices using the compounds represented by the Formulas.

Effects of the Invention

By using the mixture according to the present invention as a phosphorescent host material, it is possible to achieve a high luminous efficiency and a low driving voltage of an organic electric element, and the life span of the device can be greatly improved.

BRIEF DESCRIPTION OF THE DRAWINGS

The FIGURE is an illustration of an organic electroluminescent device according to the present invention.

100: organic electric element, 110: substrate 120: the first electrode(anode), 130: the hole injection layer 140: the hole transport layer, 141: a buffer layer 150: the emitting layer, 151: the emitting auxiliary layer 160: the electron transport layer, 170: the electron injection layer 180: the second electrode(cathode)

DETAILED DESCRIPTION

Hereinafter, some embodiments of the present invention will be described in detail. Further, in the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear.

In addition, terms, such as first, second, A, B, (a), (b) or the like may be used herein when describing components of the present invention. Each of these terminologies is not used to define an essence, order or sequence of a corresponding component but used merely to distinguish the corresponding component from other component(s). It should be noted that if a component is described as being “connected”, “coupled”, or “connected” to another component, the component may be directly connected or connected to the other component, but another component may be “connected”, “coupled” or “connected” between each component.

As used in the specification and the accompanying claims, unless otherwise stated, the following is the meaning of the term as follows.

Unless otherwise stated, the term “halo” or “halogen”, as used herein, includes fluorine, bromine, chlorine, or iodine.

Unless otherwise stated, the term “alkyl” or “alkyl group”, as used herein, has a single bond of 1 to 60 carbon atoms, and means saturated aliphatic functional radicals including a linear alkyl group, a branched chain alkyl group, a cycloalkyl group (alicyclic), an cycloalkyl group substituted with a alkyl or an alkyl group substituted with a cycloalkyl.

Unless otherwise stated, the term “haloalkyl” or “halogen alkyl”, as used herein, includes an alkyl group substituted with a halogen.

Unless otherwise stated, the term “heteroalkyl”, as used herein, means alkyl substituted one or more of carbon atoms consisting of an alkyl with hetero atom.

Unless otherwise stated, the term “alkenyl” or “alkynyl”, as used herein, has double or triple bonds of 2 to 60 carbon atoms, but is not limited thereto, and includes a linear or a branched chain group.

Unless otherwise stated, the term “cycloalkyl”, as used herein, means alkyl forming a ring having 3 to 60 carbon atoms, but is not limited thereto.

Unless otherwise stated, the term “alkoxyl group”, “alkoxy group” or “alkyloxy group”, as used herein, means an oxygen radical attached to an alkyl group, but is not limited thereto, and has 1 to 60 carbon atoms.

Unless otherwise stated, the term “alkenoxyl group”, “alkenoxy group”, “alkenyloxyl group” or “alkenyloxy group”, as used herein, means an oxygen radical attached to an alkenyl group, but is not limited thereto, and has 2 to 60 carbon atoms.

Unless otherwise stated, the term “aryloxyl group” or “aryloxy group”, as used herein, means an oxygen radical attached to an aryl group, but is not limited thereto, and has 6 to 60 carbon atoms.

Unless otherwise stated, the term “aryl group” or “arylene group”, as used herein, has 6 to 60 carbon atoms, but is not limited thereto. Herein, the aryl group or arylene group means a monocyclic and polycyclic aromatic group, and may also be formed in conjunction with an adjacent group. Examples of “aryl group” may include a phenyl group, a biphenyl group, a fluorene group, or a spirofluorene group.

The prefix “aryl” or “ar” means a radical substituted with an aryl group. For example, an arylalkyl may be an alkyl substituted with an aryl, and an arylalenyl may be an alkenyl substituted with aryl, and a radical substituted with an aryl has a number of carbon atoms as defined herein.

Also, when prefixes are named subsequently, it means that substituents are listed in the order described first. For example, an arylalkoxy means an alkoxy substituted with an aryl, an alkoxylcarbonyl means a carbonyl substituted with an alkoxyl, and an arylcarbonylalkenyl also means an alkenyl substituted with an arylcarbonyl, wherein the arylcarbonyl may be a carbonyl substituted with an aryl.

Unless otherwise stated, the term “heteroalkyl”, as used herein, means alkyl containing one or more of hetero atoms. Unless otherwise stated, the term “heteroaryl group” or “heteroarylene group”, as used herein, means a C2 to C60 aryl containing one or more of hetero atoms or arylene group, but is not limited thereto, and includes at least one of monocyclic and polycyclic rings, and may also be formed in conjunction with an adjacent group.

Unless otherwise stated, the term “heterocyclic group”, as used herein, contains one or more heteroatoms, but is not limited thereto, has 2 to 60 carbon atoms, includes any one of monocyclic and polycyclic rings, and may include heteroaliphatic ring and/or heteroaromatic ring. Also, the heterocyclic group may also be formed in conjunction with an adjacent group. Unless otherwise stated, the term “heteroatom”, as used herein, represents at least one of N, O, S, P, or Si.

Also, the term “heterocyclic group” may include a ring containing SO₂ instead of carbon consisting of cycle. For example, “heterocyclic group” includes compound below.

Unless otherwise stated, the term “aliphatic”, as used herein, means an aliphatic hydrocarbon having 1 to 60 carbon atoms, and the term “aliphatic ring”, as used herein, means an aliphatic hydrocarbon ring having 3 to 60 carbon atoms.

Unless otherwise stated, the term “ring”, as used herein, means an aliphatic ring having 3 to 60 carbon atoms, or an aromatic ring having 6 to 60 carbon atoms, or a hetero ring having 2 to 60 carbon atoms, or a fused ring formed by the combination of them, and includes a saturated or unsaturated ring.

Other hetero compounds or hetero radicals other than the above-mentioned hetero compounds include, but are not limited thereto, one or more heteroatoms.

Unless otherwise stated, the term “carbonyl”, as used herein, is represented by —COR′, wherein R′ may be hydrogen, an alkyl having 1 to 20 carbon atoms, an aryl having 6 to 30 carbon atoms, a cycloalkyl having 3 to 30 carbon atoms, an alkenyl having 2 to 20 carbon atoms, an alkynyl having 2 to 20 carbon atoms, or the combination of these.

Unless otherwise stated, the term “ether”, as used herein, is represented by —R—O—R′, wherein R or R′ may be independently hydrogen, an alkyl having 1 to 20 carbon atoms, an aryl having 6 to 30 carbon atoms, a cycloalkyl having 3 to 30 carbon atoms, an alkenyl having 2 to 20 carbon atoms, an alkynyl having 2 to 20 carbon atoms, or the combination of these.

Unless otherwise stated, the term “substituted or unsubstituted”, as used herein, means that substitution is substituted by at least one substituent selected from the group consisting of, but is not limited thereto, deuterium, halogen, an amino group, a nitrile group, a nitro group, a C₁-C₂₀ alkyl group, a C₁-C₂₀ alkoxyl group, a C₁-C₂₀ alkylamine group, a C₁-C₂₀ alkylthiopen group, a C₆-C₂₀ arylthiophene group, a C₂-C₂₀ alkenyl group, a C₂-C₂₀ alkynyl group, a C₃-C₂₀ cycloalkyl group, a C₆-C₂₀ aryl group, a C₆-C₂₀ aryl group substituted by deuterium, a C₈-C₂₀ arylalkenyl group, a silane group, a boron group, a germanium group, and a C₂-C₂₀ heterocyclic group.

Unless otherwise expressly stated, the Formula used in the present invention, as used herein, is applied in the same manner as the substituent definition according to the definition of the exponent of the following Formula.

Here, when a is an integer of 0, it means that the substituent R¹ is absent, that is, when a is 0, it means that all hydrogens are bonded to carbons forming the benzene ring, and in this case, the display of hydrogen bonded to carbon may be omitted and the chemical formula or compound may be described.

When a is an integer of 1, one substituent R¹ is bonded to any one of carbons forming a benzene ring, and when a is an integer of 2 or 3, they are respectively combined as follows, in which R¹ may be the same or different from each other, and when a is an integer of 4 to 6, and it is bonded to the carbon of the benzene ring in a similar manner, whereas the indication of hydrogen bonded to the carbon forming the benzene ring is omitted.

Hereinafter, a compound according to an aspect of the present invention and an organic electric element comprising the same will be described.

The present invention provides an organic electronic element comprising a first electrode, a second electrode, and an organic material layer formed between the first electrode and the second electrode, wherein the organic material layer comprises an emitting layer, wherein the emitting layer comprises a first host compound represented by Formula 1 and a second host compound represented by Formula 2 as the phosphorescent emitting layer.

{In Formula 1 and Formula 2,

1) M is a C₆-C₆₀ arylene group or a substituent represented by Formula 1-1,

2) A, B, C and D are each independently a C₆-C₆₀ aryl group or a C₂-C₆₀ heterocyclic group, and C is bonded to L³, D is bonded to L⁴,

3) X¹ is S or O, and X² and X³ are each independently N-L⁸-Ar⁸, O, S or CR′R″,

R′ and R″ are selected from the group consisting of hydrogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₃-C₆₀ heterocyclic group; a C₁-C₅₀ alkyl group; and -L′-N(R^(a))(R^(b)), R′ and R″ may be bonded to each other to form a spiro,

4) x is an integer of 0˜3, y is an integer of 0˜4,

5) R^(c) and R^(d) are each independently selected from a group consisting of hydrogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R^(a))(R^(b)), and R^(a) and R^(b) are each independently selected from a group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₂-C₆₀ heterocyclic group including at least one hetero atom of O, N, S, Si or P;

6) wherein, L′ is selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic,

7) Ar¹, Ar², Ar³, Ar⁴, Ar⁵, Ar⁶, Ar⁷ and Ar⁸ are each independently selected from the group consisting of a C₆-C₆₀ aryl group; a C₂-C₆₀ heterocyclic group including at least one hetero atom of O, N, S, Si or P; a fluorenyl group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; C₆-C₃₀ arylthio group; a C₆-C₃₀ aryloxy group, and Ar¹ and Ar², or Ar⁴ and Ar⁵ may be bonded to each other to form a ring,

8) L¹, L², L³, L⁴, L⁵, L⁵, L⁶, L⁷ and L⁸ are independently selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; or a C₂-C₆₀ heteroarylene group containing at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and an aliphatic hydrocarbon group;

wherein, the aryl group, fluorenyl group, arylene group, heterocyclic group, fluorenylene group, fused ring group, alkyl group, alkenyl group, alkoxy group and aryloxy group may be substituted with one or more substituents selected from the group consisting of deuterium; halogen; a silane group; siloxane group; boron group; germanium group; cyano group; nitro group; a C₁-C₂₀ alkylthio group; C₁-C₂₀ alkoxyl group; C₁-C₂₀ alkyl group; C₂-C₂₀ alkenyl group; C₂-C₂₀ alkynyl group; C₁-C₂₀ aryl group; C₁-C₂₀ aryl group substituted with deuterium; a fluorenyl group; C₂-C₂₀ heterocyclic group; C₃-C₂₀ cycloalkyl group; C₇-C₂₀ arylalkyl group and C₈-C₂₀ arylalkenyl group, wherein the substituents may be bonded to each other to form a saturated or unsaturated ring, wherein the term ‘ring’ means a C₃-C₆₀ aliphatic ring or a C₆-C₆₀ aromatic ring or a C₂-C₆₀ heterocyclic group or a fused ring formed by the combination thereof.}

Also, the present invention provides an organic electric element, wherein in Formula 1, A, B, C and D each independently include a compound represented by any one of the following formulas a-1 to a-7.

{In Formulas a-1 to a-7,

Z¹ to Z⁴⁸ are each independently CR^(e) or N,

Z¹ to Z⁴⁸ bonded to L¹ to L⁴ are carbon (C),

R^(e) is the same as the definition of R^(a),

* indicates the position to be condensed.}

Specially, the present invention provides an organic electric element, wherein L¹, L², L³, L⁴, L⁵, L⁶, L⁷ and L⁸ in Formula 1 or 2 include a compound represented by any one of the following formulas b-1 to b-13.

{In Formulas b-1 to b-13,

Y is N-L⁹-Ar⁹, O, S or CR′R″,

L⁹ is the same as the definition of L¹,

Ar⁹ is the same as the definition of Ar¹,

R′ and R″ are the same as defined above,

a, c, d and e are each independently an integer of 0 to 4 and b is an integer of 0 to 6,

f and g are each independently an integer of 0 to 3, h is an integer of 0 to 2, i is an integer of 0 or 1,

R¹, R² and R³ are each independently selected from the group consisting of hydrogen; deuterium; tritium; halogen; cyano group; nitro group; C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L^(a)-N(R^(h))(R^(i)); or in case a, b, c, d, e, f and g are 2 or more, and h is 2 or more, R¹, R² and R³ are in plural being the same or different, and a plurality of R¹ or a plurality of R² or a plurality of R³ or adjacent R¹ and R², or adjacent R² and R³ may be bonded to each other to form an aromatic or a heteroaromatic ring,

where, L^(a) is selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; a C₂-C₆₀ heterocyclic group containing at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and C₃-C₆₀ aliphatic hydrocarbon group;

R^(h) and R^(i) are each independently selected from the group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group containing at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring,

Z⁴⁹, Z⁵⁰, and Z⁵¹ are each independently CR^(g) or N,

at least one of Z⁴⁹, Z⁵⁰, and Z⁵¹ is N,

R^(g) is selected from the group consisting of hydrogen; deuterium; tritium; halogen; cyano group; nitro group; C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and adjacent R¹ and R^(g) may be bonded to each other to form an aromatic or a heteroaromatic ring.}

As another example, the present invention provides an organic electric element including a compound in which at least one of Ar¹, Ar², Ar³, Ar⁴, Ar⁵ is represented by Formula 1-2.

{In Formula 1-2,

E and F are the same as the definition of A,

X⁵ is N-L¹⁰-Ar¹⁰, O, S or CR′R″,

L¹⁰ and L¹¹ are the same as the definition of L¹,

Ar¹⁰ is the same as the definition of Ar¹,

R′ and R″ are the same as defined above.}

The first host compound represented by Formula 1 includes a compound represented by Formula 3 below.

{In Formula 3,

X¹, X², Ar¹, Ar², Ar³, Ar⁴ and Ar⁵ are the same as defined above, Z⁵², Z⁵³, Z⁵⁴ and Z⁵⁵ are each independently CR^(e) or N, and Z⁵², Z⁵³, Z⁵⁴ or Z⁵⁵ bonded to N is carbon (C), and R^(e) is the same as the definition of R^(a).}

More specifically, the present invention provides an organic electric element including a compound wherein X¹ and X² of Formula 1 are independently O or S.

Otherwise, the second host compound represented by Formula 2 includes a compound represented by any one of Formulas 4 to 7 below.

{In Formulas 4 to 7,

X², L⁵, L⁶, L⁷, Ar⁶, Ar⁷, R^(c), R^(d), x and y are the same as defined above.}

The second host compound represented by Formula 2 includes a compound represented by Formula 8 below.

{In Formula 8,

X², L⁵, L⁶, L⁷, Ar⁶, R^(c), R^(d), x and y are the same as defined above,

X⁴ is the same as the definition of X², R^(e) and R^(f) are the same as the definition of R^(d) and R^(c), n is the same as the definition of y, m is the same as the definition of x.}

The second host compound represented by Formula 2 includes compounds represented by Formulas 9 to 12 below.

{In Formulas 9 to 12,

X², L⁵, L⁶, L⁷, Ar⁶, R^(c), R^(d), x and y are the same as defined above,

R^(e) and R^(f) are the same as the definition of R^(d) and R^(c), n is the same as the definition of y, m is the same as the definition of x.}

More specially, the first host compound represented by Formula 1 includes Compound 1-1 to Compound 1-265 below.

The second host compound represented by Formula 2 includes the following compounds.

Referring to the FIGURE, the organic electric element (100) according to the present invention includes a first electrode (120) formed on a substrate (110), a second electrode (180), and an organic material layer including the compound represented by Formula 1 between the first electrode (120) and the second electrode (180). Here, the first electrode (120) may be an anode (positive electrode), and the second electrode (180) may be a cathode (negative electrode). In the case of an inverted organic electric element, the first electrode may be a cathode, and the second electrode may be an anode.

The organic material layer may include a hole injection layer (130), a hole transport layer (140), an emitting layer (150), an emitting-auxiliary layer (151), an electron transport layer (160), and an electron injection layer (170) formed in sequence on the first electrode (120). Here, the remaining layers except the emitting layer (150) may not be formed. The organic material layer may further include a hole blocking layer, an electron blocking layer, an emitting-auxiliary layer (151), an electron transport auxiliary layer, a buffer layer (141), etc., and the electron transport layer (160) and the like may serve as a hole blocking layer.

Although not shown, the organic electric element according to the present invention may further include a protective layer formed on at least one side of the first and second electrodes, which is a side opposite to the organic material layer.

Otherwise, even if the same core is used, the band gap, the electrical characteristics, the interface characteristics, and the like may vary depending on which substituent is bonded at which position, therefore the choice of core and the combination of sub-substituents associated therewith is also very important, and in particular, when the optimal combination of energy levels and T1 values and unique properties of materials (mobility, interfacial characteristics, etc.) of each organic material layer is achieved, a long lifespan and high efficiency can be achieved at the same time.

The organic electroluminescent device according to an embodiment of the present invention may be manufactured using a PVD (physical vapor deposition) method. For example, an anode is formed by depositing a metal or a conductive metal oxide or an alloy thereof on a substrate, and after forming an organic material layer including the hole injection layer (130), the hole transport layer (140), the emitting layer (150), the electron transport layer (160) and the electron injection layer (170) thereon, the organic electroluminescent device according to an embodiment of the present invention can be manufactured by depositing a material that can be used as a cathode thereon.

In addition, an emitting auxiliary layer (151) may be further formed between the hole transport layer (140) and the emitting layer (150), and an electron transport auxiliary layer may be further formed between the emitting layer (150) and the electron transport layer (160).

Accordingly, the present invention includes at least one hole transport layer between the first electrode and the emitting layer, wherein the hole transport layer includes a hole transport layer, an emitting auxiliary layer, or both, and wherein the hole transport layer includes the compound represented by Formula 1.

Also, the compounds represented by Formula 1 and by Formula 2 are mixed in a ratio of any one of 1:9 to 9:1 to be included in the emitting layer, preferably mixed in a ratio of 1:9 to 5:5, more preferably in a ratio of 2:8 or 3:7 to be included in the emitting layer.

The present invention may further include a light efficiency enhancing layer formed on at least one of the opposite side to the organic material layer among one side of the first electrode, or one of the opposite side to the organic material layer among one side of the second electrode. Also, the organic material layer is formed by one of a spin coating process, a nozzle printing process, an inkjet printing process, a slot coating process, a dip coating process or a roll-to-roll process, and since the organic material layer according to the present invention can be formed by various methods, the scope of the present invention is not limited by the method of forming the organic material layer.

The organic electric element according to an embodiment of the present invention may be a top emission type, a bottom emission type, or a double side emission type, depending on the material used.

WOLED (White Organic Light Emitting Device) is easy to realize high resolution and excellent processability, while there is an advantage that can be manufactured using the existing LCD color filter technology. Various structures for a white organic light emitting device mainly used as a backlight device have been proposed and patented. Typically, R (Red), G (Green), B (Blue) light emitting parts are arranged in a side-by-side manner, and R, G, B light emitting layers are stacked up and down, and blue (B) electroluminescence by organic emitting layer and, there is a color conversion material (CCM) method using photo-luminescence of an inorganic phosphor using light from this, and the present invention may be applied to such WOLED.

The present invention also provides an electronic device comprising a display device including the organic electric element; and a control unit for driving the display device.

According to another aspect, the present invention provides an electronic device wherein the organic electric element is at least one of an OLED, an organic solar cell, an organic photo conductor, an organic transistor and an element for monochromic or white illumination. At this time, the electronic device may be a current or future wired/wireless communication terminal, and covers all kinds of electronic devices including a mobile communication terminal such as a cellular phone, a personal digital assistant (PDA), an electronic dictionary, a point-to-multipoint (PMP), a remote controller, a navigation unit, a game player, various kinds of TVs, and various kinds of computers.

Hereinafter, Synthesis Examples of the compound represented by Formula 1 and Formula 2 according to the present invention and preparation examples of the organic electric element of the present invention will be described in detail by way of example, but are not limited to the following examples of the invention.

Synthesis Example 1

The final product 1 represented by Formula 1 according to the present invention is was prepared by the synthetic method disclosed in Korean Patent No. 10-1614739 (registered on Apr. 18, 2016) and Korean Patent Application No. 2016-0110817 (filed on Aug. 30, 2016) of the present applicant. X¹, A, B, L¹, L², L³, L⁴, M, Ar¹, Ar², Ar³, Ar⁴, Ar⁵ are the same as defined in Formula 1.

I. Synthesis of Final Product 1

After dissolving Sub 1 (1 eq.) with Toluene in a round bottom flask, Sub 2 (1 eq.), Pd₂(dba)₃ (0.03 eq.), (t-Bu)₃P (0.06 eq.), and NaOt-Bu (2 eq.) were stirred at 100° C. When the reaction was completed, the resulting compound was extracted with CH₂Cl₂ and water, and the organic layer was dried over MgSO₄ and concentrated, and the resulting compound was recrystallized with a silicagel column to obtain Final product 1.

1. Synthesis Example of 1-59

After dissolving Sub 2-59 (5.30 g, 11.97 mmol) with Toluene (120 mL) in a round bottom flask, Sub 1-59 (5.15 g, 11.97 mmol), Pd₂(dba)₃ (0.33 g, 0.36 mmol), P(t-Bu)₃ (0.4 mL, 0.72 mmol), NaOt-Bu (3.45 g, 35.90 mmol) were stirred at 100° C. When the reaction was completed, the resulting compound was extracted with CH₂Cl₂ and water, and the organic layer was dried over MgSO₄ and concentrated, and the resulting compound was recrystallized with a silicagel column to obtain 1-59 (7.96 g, yield: 84%)

2. Synthesis Example of 1-195

Sub 1-195 (4.10 g, 7.47 mmol), Sub 2-195 (2.42 g, 7.47 mmol), Pd₂(dba)₃ (0.21 g, 0.22 mmol), P(t-Bu)₃ (0.2 mL, 0.45 mmol), NaOt-Bu (2.15 g, 22.42 mmol) 1-59 (7.96 g, yield: 84%) were added, and the same procedure as described in the synthesis method of 1-59 was carried out to obtain the product 1-195. (5.33 g, yield:90%).

Synthesis Example 2

The final product represented by Formula 2 according to the present invention may be prepared by reacting Sub 3 and Sub 4 as shown in Scheme 2 below, but is not limited thereto.

Synthesis Example of 1′-1

After placing Sub 1(1) (34.7 g, 80 mmol) and Sub 2(1) (30.9 g, 80 mmol), K₂CO₃ (19.3 g, 140 mmol), Pd(PPh₃)₄ (2.8 g, 2.4 mmol) in a round bottom flask, THF and water were added to dissolve, and then refluxed at 80° C. for 12 hours. When the reaction was completed, the temperature of the reaction product was cooled to room temperature, extracted with CH₂Cl₂, and washed with water. The organic layer was dried over MgSO₄, concentrated, and the resulting organic material was separated using a silicagel column to obtain the desired product (37.4 g, 71%).

Synthesis Example of 1′-6

Sub 1(6) (44.6 g, 80 mmol) and Sub 2(2) (30.9 g, 80 mmol) were used to obtain a product (43.2 g, 69%) using the synthesis method of 1′-1.

Synthesis Example of 1′-12

Sub 1(12) (42.7 g, 80 mmol) and Sub 2(33) (34.9 g, 80 mmol) were used to obtain a product (42.7 g, 66%) using the synthesis method of 1′-1.

Synthesis Example of 1-33

Sub 1(27) (40.8 g, 80 mmol) and Sub 2(9) (43.1 g, 80 mmol) were used to obtain a product (51.0 g, 72%) using the synthesis method of 1′-1.

Synthesis Example of 1′-44

Sub 1(28) (40.8 g, 80 mmol) and Sub 2(10) (37.0 g, 80 mmol) were used to obtain a product (45.4 g, 70%) using the synthesis method of 1′-1.

Synthesis Example of 1′-53

Sub 1(34) (44.0 g, 80 mmol) and Sub 2(29) (29.6 g, 80 mmol) were used to obtain a product (41.2 g, 68%) using the synthesis method of 1′-1.

Synthesis Example of 1′-64

Sub 1(37) (48.2 g, 80 mmol) and Sub 2(34) (34.9 g, 80 mmol) were used to obtain a product (45.6 g, 71%) using the synthesis method of 1′-1.

Synthesis Example of 1′-75

Sub 1(25) (34.7 g, 80 mmol) and Sub 2(35) (41.8 g, 80 mmol) were used to obtain a product (46.4 g, 73%) using the synthesis method of 1′-1.

Synthesis Example of 2-1

Sub 1(1) (34.7 g, 80 mmol) and Sub 2(27) (37.0 g, 80 mmol) were used to obtain a product (42.3 g, 72%) using the synthesis method of 1′-1.

Synthesis Example of 2-22

Sub 1(38) (50.7 g, 80 mmol) and Sub 2(24) (37.0 g, 80 mmol) were used to obtain a product (51.6 g, 69%) using the synthesis method of 1′-1.

Synthesis Example of 2-33

Sub 1(27) (40.8 g, 80 mmol) and Sub 2(36) (49.2 g, 80 mmol) were used to obtain a product (53.9 g, 70%) using the synthesis method of 1′-1.

Synthesis Example of 2-40

Sub 1(25) (34.7 g, 80 mmol) and Sub 2(37) (43.1 g, 80 mmol) were used to obtain a product (44.7 g, 69%) using the synthesis method of 1′-1.

Synthesis Example of 2-51

Sub 1(33) (36.0 g, 80 mmol) and Sub 2(38) (35.7 g, 80 mmol) were used to obtain a product (41.1 g, 70%) using the synthesis method of 1′-1.

Synthesis Example of 2-55

Sub 1(39) (42.1 g, 80 mmol) and Sub 2(23) (37.0 g, 80 mmol) were used to obtain a product (44.9 g, 68%) using the synthesis method of 1′-1.

Synthesis Example of 2-58

Sub 1(25) (34.7 g, 80 mmol) and Sub 2(39) (47.9 g, 80 mmol) were used to obtain a product (45.9 g, 66%) using the synthesis method of 1′-1.

Synthesis Example of 3-10

Sub 1(37) (28.6 g, 80 mmol) and Sub 2(10) (37.0 g, 80 mmol) were used to obtain a product (38.9 g, 74%) using the synthesis method of 1′-1.

Synthesis Example of P-41

Core 2 (5 g, 14 mmol), Sub 1 (4.6 g, 15.2 mmol), Pd(PPh₃)₄ (0.5 g, 0.4 mmol), K₂CO₃ (5.7 g, 41.3 mmol), THF and water were added in a round bottom flask and stirred at 90° C. After the reaction was completed, the reaction mixture was extracted with CH₂Cl₂ and water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was separated by silicagel column chromatography and recrystallized to obtain 4.6 g of P-41. (yield:57%)

Synthesis Example of P-91

Core 1 (5 g, 14 mmol), Sub 9 (5.8 g, 15.4 mmol), Pd(PPh₃)₄ (0.5 g, 0.4 mmol), K₂CO₃ (5.8 g, 41.9 mmol), THF and water were added in a round bottom flask and stirred at 90° C. After the reaction was completed, the reaction mixture was extracted with CH₂Cl₂ and water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was separated by silicagel column chromatography and recrystallized to obtain 4.7 g of P-91. (yield:51%)

Synthesis Example of P-106

Core 1 (5 g, 14 mmol), Sub 16 (5.8 g, 15.4 mmol), Pd(PPh₃)₄ (0.5 g, 0.4 mmol), K₂CO₃ (5.8 g, 41.9 mmol), THF and water were added in a round bottom flask and stirred at 90° C. After the reaction was completed, the reaction mixture was extracted with CH₂Cl₂ and water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was separated by silicagel column chromatography and recrystallized to obtain 5.8 g of P-106. (yield:63%)

Synthesis Example of P-146

Core 11 (5 g, 14 mmol), Sub 2 (5.8 g, 15.4 mmol), Pd(PPh₃)₄ (0.5 g, 0.4 mmol), K₂CO₃ (5.8 g, 41.9 mmol), THF and water were added in a round bottom flask and stirred at 90° C. After the reaction was completed, the reaction mixture was extracted with CH₂Cl₂ and water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was separated by silicagel column chromatography and recrystallized to obtain 4.7 g of P-146. (yield:51%)

Synthesis Example of P-4

Core 1 (5 g, 14 mmol), Sub 6 (5.9 g, 15.4 mmol), Pd(PPh₃)₄ (0.5 g, 0.4 mmol), K₂CO₃ (5.8 g, 41.9 mmol), THF and water were added in a round bottom flask and stirred at 90° C. After the reaction was completed, the reaction mixture was extracted with CH₂Cl₂ and water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was separated by silicagel column chromatography and recrystallized to obtain 6.1 g of P-4. (yield:66%)

Synthesis Example of 4-1

Sub 1-1′ (50 g, 98.04 mmol) was added to around bottom flask and dissolve with THF (359 mL), Sub 2-1′(52.51 g, 117.65 mmol), Pd(PPh₃)₄ (4.53 g, 3.92 mmol), K₂CO₃ (40.65 g, 294.12 mmol) and water (180 mL) were added and stirred to reflux. After the reaction was completed, the reaction mixture was extracted with ether and water. The organic layer was dried over MgSO₄ and concentrated. Thereafter, the concentrate was passed through a silicagel column and recrystallized to obtain 64.61 g of a product. (Yield: 83%)

Synthesis Example of 5-3

Sub 1-1″ (60 g, 133.35 mmol) was added to a round bottom flask and dissolve with THF (489 mL), Sub 2-3″ (58.28 g, 160.01 mmol), Pd(PPh₃)₄ (6.16 g, 5.33 mmol), K₂CO₃ (55.29 g, 400.04 mmol), and water (244 mL) were added and stirred to reflux. When the reaction is complete, the resulting compound was extracted with ether and water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was separated by silicagel column chromatography and recrystallized to obtain 73.40 g of the product. (yield:75%)

TABLE 1 compound FD-MS compound FD-MS 1′-1 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 1′-2 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 1′-3 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 1′-4 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 1′-5 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) 1′-6 m/z = 781.22(C₅₅H₃₁N₃OS = 781.93) 1′-7 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 1′-8 m/z = 721.22(C₅₀H₃₁N₃OS = 721.88) 1′-9 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 1′-10 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 1′-11 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-12 m/z = 807.23(C₅₇H₃₃N₃OS = 807.97) 1′-13 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 1′-14 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 1′-15 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-16 m/z = 859.27(C₆₁H₃₇N₃OS = 860.05) 1′-17 m/z = 807.23(C₅₇H₃₃N₃OS = 807.97) 1′-18 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) 1′-19 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 1′-20 m/z = 859.27(C₆₁H₃₇N₃OS = 860.05) 1′-21 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-22 m/z = 857.25(C₆₁H₃₅N₃OS = 858.03) 1′-23 m/z = 833.25(C₅₉H₃₅N₃OS = 834.01) 1′-24 m/z = 825.23(C₅₇H₃₂FN₃OS = 825.96) 1′-25 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 1′-26 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-27 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 1′-28 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 1′-29 m/z = 732.22(C₅₁H₃₁N₃OS = 733.89) 1′-30 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-31 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 1′-32 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 1′-33 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 1′-34 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-35 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-36 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 1′-37 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-38 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-39 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 1′-40 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 1′-41 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 1′-42 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-43 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-44 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 1′-45 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 1′-46 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 1′-47 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 1′-48 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 1′-49 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 1′-50 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 1′-51 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 1′-52 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 1′-53 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) 1′-54 m/z = 781.22(C₅₅H₃₁N₃OS = 781.93) 1′-55 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 1′-56 m/z = 721.22(C₅₀H₃₁N₃OS = 721.88) 1′-57 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 1′-58 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 1′-59 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 1′-60 m/z = 807.23(C₅₇H₃₃N₃OS = 807.97) 1′-61 m/z = 723.18(C₄₉H₂₉N₃S₂ = 723.91) 1′-62 m/z = 723.18(C₄₉H₂₉N₃S₂ = 723.91) 1′-63 m/z = 749.20(C₅₁H₃₁N₃S₂ = 749.95) 1′-64 m/z = 875.24(C₆₁H₃₇N₃S₂ = 876.11) 1′-65 m/z = 823.21(C₅₇H₃₃N₃S₂ = 824.03) 1′-66 m/z = 773.20(C₅₃H₃₁N₃S₂ = 773.97) 1′-67 m/z = 799.21(C₅₅H₃₃N₃S₂ = 800.01) 1′-68 m/z = 875.24(C₆₁H₃₇N₃S₂ = 876.11) 1′-69 m/z = 749.20(C₅₁H₃₁N₃S₂ = 749.95) 1′-70 m/z = 873.23(C₆₁H₃₅N₃S₂ = 874.09) 1′-71 m/z = 849.23(C₅₉H₃₅N₃S₂ = 850.07) 1′-72 m/z = 791.19(C₅₃H₃₀FN₃S₂ = 791.96) 1′-73 m/z = 641.21(C₄₅H₂₇N₃O₂ = 641.73) 1′-74 m/z = 717.24(C₅₁H₃₁N₃O₂ = 717.83) 1′-75 m/z = 798.30(C₅₇H₃₀D₅N₃O₂ = 799.0) 1′-76 m/z = 843.29(C₆₁H₃₇N₃O₂ = 843.99) 1′-77 m/z = 717.24(C₅₁H₃₁N₃O₂ = 717.83) 1′-78 m/z = 717.24(C₅₁H₃₁N₃O₃ = 717.83) 1′-79 m/z = 641.21(C₄₅H₂₇N₃O₂ = 641.73) 1′-80 m/z = 793.27(C₅₇H₃₅N₃O₂ = 793.93) 1′-81 m/z = 869.30(C₆₃H₃₉N₃O₂ = 870.02) 1′-82 m/z = 717.24(C₅₁H₃₁N₃O₂ = 717.83) 1′-83 m/z = 722.27(C₅₁H₂₆D₅N₃O₂ = 722.9) 1′-84 m/z = 793.27(C₅₇H₃₅N₃O₂ = 793.93) 2-1 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 2-2 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 2-3 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 2-4 m/z = 859.27(C₆₁H₃₇N₃OS = 860.05) 2-5 m/z = 833.25(C₅₉H₃₅N₃OS = 834.01) 2-6 m/z = 857.25(C₆₁H₃₅N₃OS = 858.03) 2-7 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-8 m/z = 797.25(C₅₆H₃₅N₃OS = 797.98) 2-9 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 2-10 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 2-11 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-12 m/z = 883.27(C₆₃H₃₇N₃OS = 884.07) 2-13 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 2-14 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 2-15 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-16 m/z = 935.30(C₆₇H₄₁N₃OS = 936.15) 2-17 m/z = 883.27(C₆₃H₃₇N₃OS = 884.07) 2-18 m/z = 833.25(C₅₉H₃₅N₃OS = 834.01) 2-19 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-20 m/z = 909.28(C₆₅H₃₉N₃OS = 910.11) 2-21 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-22 m/z = 933.28(C₆₇H₃₉N₃OS = 934.13) 2-23 m/z = 909.28(C₆₅H₃₉N₃OS = 910.11) 2-24 m/z = 851.24(C₅₉H₃₄FN₃OS = 852.00) 2-25 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 2-26 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-27 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-28 m/z = 935.30(C₆₇H₄₁N₃OS = 936.15) 2-29 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-30 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-31 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 2-32 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-33 m/z = 961.31(C₆₉H₄₃N₃OS = 962.18) 2-34 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-35 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-36 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-37 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-38 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-39 m/z = 961.31(C₆₉H₄₃N₃OS = 962.18) 2-40 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-41 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-42 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-43 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-44 m/z = 1032.40(C₇₄H₅₄N₃OS = 1033.33) 2-45 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-46 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-47 m/z = 961.31(C₆₉H₄₃N₃OS = 962.18) 2-48 m/z = 859.27(C₆₁H₃₇N₃OS = 860.08) 2-49 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-50 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 2-51 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 2-52 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 2-53 m/z = 977.29(C₆₉H₄₃N₃S₂ = 978.24) 2-54 m/z = 825.23(C₅₇H₃₅N₃S₂ = 826.05) 2-55 m/z = 825.23(C₅₇H₃₅N₃S₂ = 826.05) 2-56 m/z = 901.26(C₆₃H₃₉N₃S₂ = 902.15) 2-57 m/z = 869.30(C₆₃H₃₉N₃O₂ = 870.02) 2-58 m/z = 869.30(C₆₃H₃₉N₃O₂ = 870.02) 2-59 m/z = 945.34(C₆₉H₄₃N₃O₂ = 946.12) 2-60 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 3-1 m/z = 581.16(C₃₉H₂₃N₃OS = 581.69) 3-2 m/z = 581.16(C₃₉H₂₃N₃OS = 581.69) 3-3 m/z = 581.16(C₃₉H₂₃N₃OS = 581.69) 3-4 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 3-5 m/z = 631.17(C₄₃H₂₅N₃OS = 631.75) 3-6 m/z = 731.20(C₅₁H₂₉N₃OS = 731.87) 3-7 m/z = 581.16(C₃₉H₂₃N₃OS = 581.69) 3-8 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 3-9 m/z = 581.16(C₃₉H₂₃N₃OS = 581.69) 3-10 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 3-11 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 3-12 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 3-13 m/z = 631.17(C₄₃H₂₅N₃OS = 631.75) 3-14 m/z = 581.16(C₃₉H₂₃N₃OS = 581.69) 3-15 m/z = 581.16(C₃₉H₂₃N₃OS = 581.69) 3-16 m/z = 799.21(C₅₅H₃₃N₃S₂ = 800.01) 3-17 m/z = 647.15(C₄₃H₂₅N₃S₂ = 647.81) 3-18 m/z = 747.18(C₅₁H₂₉N₃S₂ = 747.93) 3-19 m/z = 565.18(C₃₉H₂₃N₃O₂ = 565.63) 3-20 m/z = 641.21(C₄₅H₂₇N₃O₂ = 641.73) 3-21 m/z = 722.27(C₅₁H₂₆D₅N₃S₂ = 722.86) 3-22 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 3-23 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 3-24 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 3-25 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 3-26 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 3-27 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 3-28 m/z = 859.27(C₆₁H₃₇N₃OS = 860.05) 3-29 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 3-30 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 3-31 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 3-32 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 3-33 m/z = 885.28(C₆₃H₃₉N₃OS = 886.09) 3-34 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) 3-35 m/z = 673.16(C₄₅H₂₇N₃S₂ = 673.85) 3-36 m/z = 793.27(C₅₇H₃₅N₃O₂ = 793.93) P-1 m/z = 581.16(C₃₉H₂₃N₃OS = 581.69) P-2 m/z = 631.17(C₄₃H₂₅N₃OS = 631.75) P-3 m/z = 631.17(C₄₃H₂₅N₃OS = 631.75) P-4 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) P-5 m/z = 681.19(C₄₇H₂₇N₃OS = 681.81) P-6 m/z = 631.17(C₄₃H₂₅N₃OS = 631.75) P-7 m/z = 631.17(C₄₃H₂₅N₃OS = 631.75) P-8 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) P-9 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) P-10 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) P-11 m/z = 586.19(C₃₉H₁₈D₅N₃OS = 586.7) P-12 m/z = 681.19(C₄₇H₂₇N₃OS = 681.81) P-13 m/z = 681.19(C₄₇H₂₇N₃OS = 68 1.81) P-14 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-15 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-16 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-17 m/z = 636.20(C₄₃H₂₀D₅N₃OS = 636.8) P-18 m/z = 681.19(C₄₇H₂₇N₃OS = 681.81) P-19 m/z = 681.19(C₄₇H₂₇N₃OS = 681.81) P-20 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-21 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-22 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-23 m/z = 636.20(C₄₃H₂₀D₅N₃OS = 636.8) P-24 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-25 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-26 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-27 m/z = 733.22(C₅₁H₃₁N₃OS = 73 3.89) P-28 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-29 m/z = 662.22(C₄₅H₂₂D₅N₃OS = 662.8) P-30 m/z = 662.22(C₄₅H₂₂D₅N₃OS = 662.82) P-3 1 m/z = 581.16(C₃₉H₂₃N₃OS = 581.69) P-32 m/z = 631.17(C₄₃H₂₅N₃OS = 631.75) P-33 m/z = 631.17(C₄₃H₂₅N₃OS = 631.75) P-34 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) P-35 m/z = 681.19(C₄₇H₂₇N₃OS = 681.81) P-36 m/z = 631.17(C₄₃H₂₅N₃OS = 631.75) P-37 m/z = 631.17(C₄₃H₂₅N₃OS = 631.75) P-38 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) P-39 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) P-40 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) P-41 m/z = 586.19(C₃₉H₁₈D₅N₃OS = 586.7) P-42 m/z = 681.19(C₄₇H₂₇N₃OS = 681.81) P-43 m/z = 681.19(C₄₇H₂₇N₃OS = 681.81) P-44 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-45 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-46 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-47 m/z = 636.20(C₄₃H₂₀D₅N₃OS = 636.8) P-48 m/z = 681.19(C₄₇H₂₇N₃OS = 681.81) P-49 m/z = 681.19(C₄₇H₂₇N₃OS = 681.81) P-50 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-51 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-52 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-53 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-54 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-55 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-56 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-57 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-58 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-59 m/z = 662.22(C₄₅H₂₂DN₃OS = 662.82) P-60 m/z = 662.22(C₄₅H₂₂DN₃OS = 662.82) P-61 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) P-62 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-63 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-64 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-65 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) P-66 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-67 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-68 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-69 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-70 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-71 m/z = 662.22(C₄₅H₂₂D₅N₃OS = 662.8) P-72 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) P-73 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) P-74 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) P-75 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) P-76 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) P-77 m/z = 712.23(C₄₉H₂₄D₅N₃OS = 712.9) P-78 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) P-79 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) P-80 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) P-81 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) P-82 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) P-83 m/z = 712.23(C₄₉H₂₄D₅N₃OS = 712.9) P-84 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) P-85 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) P-86 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) P-87 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) P-88 m/z = 809.25(C₅₇H₃₅N₃OS = 809.99) P-89 m/z = 738.25(C₅₁H₂₆D₅N₃OS = 738.9) P-90 m/z = 738.25(C₅₁H₂₆D₅N₃OS = 738.92) P-91 m/z = 662.22(C₄₅H₂₂DN₃OS = 662.82) P-92 m/z = 712.23(C₄₉H₂₄D₅N₃OS = 712.88) P-93 m/z = 712.23(C₄₉H₂₄D₅N₃OS = 712.9) P-94 m/z = 738.25(C₅₁H₂₆D₅N₃OS = 738.92) P-95 m/z = 762.25(C₅₃H₂₆D₅N₃OS = 762.9) P-96 m/z = 712.23(C₄₉H₂₄D₅N₃OS = 712.88) P-97 m/z = 712.23(C₄₉H₂₄D₅N₃OS = 712.9) P-98 m/z = 738.25(C₅₁H₂₆D₅N₃OS = 738.92) P-99 m/z = 738.25(C₅₁H₂₆D₅N₃OS = 738.9) P-100 m/z = 738.25(C₅₁H₂₆D₅N₃OS = 738.92) P-101 m/z = 667.2(C₄₅H₁₇D₁₀N₃OS = 667.9) P-102 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-103 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-104 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-105 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-106 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) P-107 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-108 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-109 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-110 m/z = 757.22(C₅₃H₃₁N₃O = 757.91) P-111 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-112 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) P-113 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-114 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-115 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) P-116 m/z = 662.22(C₄₅H₂₂D₅N₃OS = 662.82) P-117 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) P-118 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) P-119 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) P-120 m/z = 783.23(C₅₅H₃₃N₃OS = 783.95) 4-1 m/z = 793.27(C₅₇H₃₅N₃O₂ = 793.93) 4-2 m/z = 869.30(C₆₃H₃₉N₃O₂ = 870.02) 4-4 m/z = 798.3(C₅₇H₃₀D₅N₃O₂ = 798.96) 4-7 m/z = 919.32(C₆₇H₄₁N₃O₂ = 920.08) 4-8 m/z = 843.29(C₆₁H₃₇N₃O₂ = 843.99) 4-10 m/z = 945.34(C₆₉H₄₃N₃O₂ = 946.12) 4-11 m/z = 944.32(C₆₈H₄₀N₄O₂ = 945.09) 4-12 m/z = 970.33(C₇₀H₄₂N₄O₂ = 971.13) 5-1 m/z = 657.19(C₄₅H₂₇N₃OS = 657.79) 5-2 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 5-3 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 5-4 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 5-7 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 5-8 m/z = 757.22(C₅₃H₃₁N₃OS = 757.91) 5-9 m/z = 859.27(C₆₁H₃₇N₃OS = 860.05) 5-10 m/z = 707.20(C₄₉H₂₉N₃OS = 707.85) 5-11 m/z = 808.23(C₅₆H₃₂N₄OS = 808.96) 5-12 m/z = 890.31(C₆₃H₃₄D₅N₃OS = 891.1) 5-13 m/z = 824.24(C₅₅H₃₂N₆OS = 824.96) 5-14 m/z = 752.20(C₅₀H₂₉FN₄OS = 752.87) 5-15 m/z = 765.26(C₅₁H₃₅N₅OS = 765.94) 5-16 m/z = 765.17(C₄₉H₂₇N₅OS₂ = 765.91) 5-17 m/z = 807.23(C₅₇H₃₃N₃OS = 807.97) 5-18 m/z = 833.25(C₅₉H₃₅N₃OS = 834.01) 5-19 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89) 5-20 m/z = 733.22(C₅₁H₃₁N₃OS = 733.89)

Evaluation of Manufacture of Organic Electric Element Example 1) Manufacture and Evaluation of Green Organic Light Emitting Diode

First, on an ITO layer(anode) formed on a glass substrate, N¹-(naphthalen-2-yl)-N⁴,N⁴-bis(4-(naphthalen-2-yl(phenyl)amino)phenyl)-N¹-phenylbenzene-1,4-diamine (hereinafter will be abbreviated as 2-TNATA) film was vacuum-deposited as a hole injection layer to form a thickness of 60 nm. Subsequently, 4,4-bis[N-(1-naphthyl)-N-phenylamino]biphenyl (hereinafter abbreviated as -NPD) was vacuum deposited to form a hole transport layer with a thickness of 60 nm. A mixture obtained by mixing the compounds represented by Formulas 1 and 2 as a host on the hole transport layer at 60:40 was used, and as a dopant, an emitting layer having a thickness of 30 nm was deposited on the hole transport layer by doping Ir(ppy)₃ [tris(2-phenylpyridine)-iridium] at 95:5 weight. (1,1′-bisphenyl)-4-oleato) bis(2-methyl-8-quinolinoleato) aluminum (hereinafter abbreviated as BAlq) was vacuum deposited to a thickness of 10 nm as a hole blocking layer, and Tris(8-quinolinol) aluminum (hereinafter abbreviated as Alq3) was formed as an electron transport layer to a thickness of 40 nm. Thereafter, as an electron injection layer, LiF, an alkali metal halide, was deposited to a thickness of 0.2 nm, Subsequently, Al was deposited to a thickness of 150 nm and used as a cathode to manufacture an organic electric element.

To the OLEDs which were manufactured by examples and comparative examples, a forward bias direct current voltage was applied, and electroluminescent (EL) properties were measured using PR-650 of Photoresearch Co., and T95 life was measured using a life measuring apparatus manufactured by McScience Inc. with a reference luminance of 5000 cd/m². In the following table, the manufacture of a device and the results of evaluation are shown.

Comparative Example 1

An organic electric element was manufactured in the same manner as in Example 1, except that Comparative Compound A alone was used as a host.

Comparative Example 2

An organic electric element was manufactured in the same manner as in Example 1, except that 1′-25 was used alone as a host.

Comparative Example 3

An organic electric element was manufactured in the same manner as in Example 1, except that P-26 was used alone as a host.

Comparative Example 4

An organic electric element was manufactured in the same manner as in Example 1, except that Comparative Compound A and the compound represented by P-26 were mixed and used as a host.

Comparative Compound A

TABLE 2 Current Second Density Brightness Efficiency( CIE First host host Voltage (mA/cm²) (cd/m²) cd/A) T(95) X Y comparative comparative — 5.6 37.6 5000.0 13.3 32.7 0.33 0.63 example1 compound A comparative — 1′-25 5.3 15.7 5000.0 32.0 60.8 0.32 0.65 example2 comparative — P-26 5.1 14.9 5000.0 33.6 58.2 0.33 0.64 example3 comparative comparative P-26 4.9 13.5 5000.0 37.1 98.6 0.33 0.61 example4 compound A example1 1-59 1′-25 4.1 11.6 5000.0 43.1 142.4 0.35 0.65 example2 1-59 P-8 3.9 11.8 5000.0 42.5 136.8 0.30 0.61 example3 1-59 P-26 4.0 11.6 5000.0 43.2 137.4 0.31 0.61 example4 1-59 P-69 4.2 11.5 5000.0 43.4 143.3 0.31 0.62 example5 1-59 4-5 4.0 11.3 5000.0 44.2 136.2 0.31 0.62 example6 1-59 5-2 4.1 11.8 5000.0 42.5 141.9 0.33 0.62 example7 1-59 6-4 3.9 11.7 5000.0 42.8 135.2 0.35 0.64 example8 1-16 1′-25 4.2 11.6 5000.0 43.2 133.5 0.33 0.61 example9 1-16 P-8 4.2 11.5 5000.0 43.3 135.8 0.31 0.61 example10 1-16 P-26 4.2 11.6 5000.0 43.0 138.6 0.34 0.61 example11 1-16 P-69 4.1 11.6 5000.0 43.1 139.2 0.31 0.61 example12 1-16 4-5 4.2 11.6 5000.0 43.0 131.6 0.31 0.62 example13 1-16 5-2 4.2 11.9 5000.0 42.0 131.7 0.34 0.61 example14 1-16 6-4 4.2 11.8 5000.0 42.5 138.4 0.32 0.65 example15 1-66 1′-25 4.4 11.9 5000.0 42.2 126.5 0.31 0.63 example16 1-66 P-8 4.3 12.2 5000.0 40.9 130.7 0.33 0.65 example17 1-66 P-26 4.4 12.3 5000.0 40.6 125.3 0.34 0.62 example18 1-66 P-69 4.4 11.8 5000.0 42.4 128.8 0.32 0.65 example19 1-66 4-5 4.3 12.3 5000.0 40.5 133.0 0.34 0.62 example20 1-66 5-2 4.3 12.3 5000.0 40.6 130.9 0.31 0.60 example21 1-66 6-4 4.4 12.0 5000.0 41.8 134.4 0.33 0.63 example22 1-181 1′-25 4.4 12.2 5000.0 41.1 123.6 0.33 0.64 example23 1-181 P-8 4.4 12.4 5000.0 40.4 129.0 0.32 0.64 example24 1-181 P-26 4.4 12.6 5000.0 39.7 123.8 0.33 0.63 example25 1-181 P-69 4.4 12.1 5000.0 41.3 121.6 0.32 0.65 example26 1-181 4-5 4.5 12.5 5000.0 39.9 125.9 0.33 0.62 example27 1-181 5-2 4.4 12.1 5000.0 41.5 129.0 0.30 0.63 example28 1-181 6-4 4.4 12.6 5000.0 39.8 126.7 0.34 0.63 example29 1-65 1′-25 4.6 12.9 5000.0 38.7 119.8 0.31 0.64 example30 1-65 P-8 4.6 12.5 5000.0 39.9 121.7 0.31 0.64 example31 1-65 P-26 4.5 12.9 5000.0 38.7 123.7 0.32 0.61 example32 1-65 P-69 4.6 12.4 5000.0 40.3 119.7 0.31 0.61 example33 1-65 4-5 4.6 12.4 5000.0 40.3 118.0 0.34 0.63 example34 1-65 5-2 4.6 12.9 5000.0 38.8 122.9 0.31 0.65 example35 1-65 6-4 4.6 12.6 5000.0 39.8 121.2 0.30 0.63 example36 1-139 1′-25 4.6 12.7 5000.0 39.3 115.0 0.34 0.63 example37 1-139 P-8 4.6 12.9 5000.0 38.8 119.3 0.34 0.62 example38 1-139 P-26 4.5 12.9 5000.0 38.8 115.6 0.34 0.61 example39 1-139 P-69 4.6 12.5 5000.0 39.9 117.3 0.34 0.65 example40 1-139 4-5 4.5 12.7 5000.0 39.4 122.5 0.32 0.62 example41 1-139 5-2 4.6 12.8 5000.0 39.1 121.8 0.32 0.63 example42 1-139 6-4 4.6 12.5 5000.0 39.9 121.1 0.32 0.63 example43 1-1 1′-25 4.6 12.7 5000.0 39.3 112.6 0.30 0.62 example44 1-1 P-8 4.5 12.9 5000.0 38.8 119.8 0.33 0.64 example45 1-1 P-26 4.5 12.9 5000.0 38.7 115.0 0.31 0.65 example46 1-1 P-69 4.5 13.0 5000.0 38.6 112.3 0.32 0.60 example47 1-1 4-5 4.5 13.1 5000.0 38.2 112.7 0.34 0.64 example48 1-1 5-2 4.6 12.8 5000.0 39.0 111.1 0.34 0.62 example49 1-1 6-4 4.5 12.9 5000.0 38.7 114.6 0.31 0.65 example50 1-76 1′-25 4.1 11.6 5000.0 43.0 133.5 0.34 0.62 example51 1-76 P-8 4.1 11.7 5000.0 42.8 137.3 0.31 0.60 example52 1-76 P-26 4.1 11.5 5000.0 43.4 131.6 0.30 0.62 example53 1-76 P-69 4.0 11.9 5000.0 42.1 137.4 0.30 0.63 example54 1-76 4-5 4.1 11.6 5000.0 43.2 135.2 0.32 0.61 example55 1-76 5-2 4.1 11.7 5000.0 42.7 135.7 0.32 0.60 example56 1-76 6-4 4.3 11.7 5000.0 42.8 133.5 0.31 0.63

As can be seen from the results of Table 2, when the material for an organic electric element of the present invention represented by Formula 1 and Formula 2 is mixed and used as a phosphorescent host (Examples 1 to 56), compared to devices using a single compound (Comparative Examples 1 to 3) or device mixed with a comparative compound (Comparative Examples 4), the driving voltage, efficiency, and lifespan are significantly improved.

In detail, when Comparative Compound A was used as a phosphorescent host as a single material, both driving voltage, efficiency, and lifespan showed relatively poor results. When the compound represented by Formula 2 was used alone, there was a slight increase in driving and efficiency compared to the comparative compounds, but since Comparative Compound A and the compound represented by Formula 2 were mixed and used as a phosphorescent host, all the effects were improved than when used as a single substance.

Therefore, when the comparative compound A with strong hole transport ability and the compound represented by Formula 2 are mixed, the effect can be improved when a compound with poor performance as a single host is mixed with a compound with good charge balance.

In addition, it can be seen that Examples 1 to 56 in which the compounds of Formula 1 and Formula 2 of the present invention were mixed and used as a host were significantly improved than in Comparative Examples 1 to 4.

Based on the above experimental results, the present inventors determined that in the case of a mixture of the compound of Formula 1 and the compound of Formula 2, each of the compounds has novel properties other than those of the compound, and measured the PL lifetime using the compound of Formula 1, the compound of Formula 2, and the mixture of the present invention, respectively. As a result, it was confirmed that when the compounds of the present invention, Formula 1 and Formula 2, were mixed, a new PL wavelength was formed unlike the single compound, and the decrease and disappearance time of the newly formed PL wavelength increased from about 60 times to about 360 times less than the decrease and disappearance time of each of the compounds of Formula 1 and Formula 2. It is considered when mixed with the compound of the present invention, not only electrons and holes are moved through the energy level of each compound, but also the efficiency and life span are increased by electron, hole transport or energy transfer by a new region (exciplex) having a new energy level formed due to mixing. As a result, when the mixture of the present invention is used, the mixed thin film is an important example showing exciplex energy transfer and light emitting process.

Also, the reason why the combination of the present invention is superior to Comparative Examples 4 in which a comparative compound is mixed and used as a phosphorescent host is that the hole characteristics are improved by using a compound containing dibenzothiophene or dibenzofuran between amine groups and has a good electrochemical synergy effect with the compound represented by Formula 2, which has strong electron properties. Accordingly, the charge balance between holes and electrons in the emitting layer is increased, so that light emission is well performed inside the emitting layer rather than the hole transport layer interface, thereby reducing deterioration at the HTL interface, maximizing the driving voltage, efficiency, and lifespan of the entire device.

Example 2) Manufacture and Evaluation of Green Organic Light Emitting Diode by Mixing Ratio

TABLE 3 Mixing ratio (first First Second host:second Current Brightness Lifetime host host host) Voltage Density (cd/m2) Efficiency T(95) example57 1-59 1′-25 7:3 4.1 11.2 5000.0 44.5 140.1 example58 5:5 4.1 11.7 5000.0 42.9 133.6 example59 4:6 4.0 12.0 5000.0 41.8 127.7 example60 3:7 4.2 12.2 5000.0 41.1 113.1 example61 1-66 P-26 7:3 4.1 12.1 5000.0 42.6 137.3 example62 5:5 4.1 12.0 5000.0 41.5 133.9 example63 4:6 4.0 12.0 5000.0 41.5 129.2 example64 3:7 4.2 12.2 5000.0 40.9 116.9

As shown in Table 3, a device was manufactured and measured in the same manner as in Example 1 by using a mixture of the compounds of the present invention in different ratios (7:3, 5:5, 4:6, 3:7). As a result of measuring by ratio, in the case of 7:3, it was similar to the result of Example 1, which was measured as 6:4, but in the case of 5:5, 4:6, and 3:7 where the ratio of the first host decreases, the results of driving voltage, efficiency, and lifespan gradually declined. This can be explained because when an appropriate amount of the compound represented by Formula 1 having strong hole properties such as 7:3 and 4:6 is mixed, the charge balance in the emitting layer is maximized.

Although exemplary embodiments of the present invention have been described for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. Therefore, the embodiment disclosed in the present invention is intended to illustrate the scope of the technical idea of the present invention, and the scope of the present invention is not limited by the embodiment.

The scope of the present invention shall be construed on the basis of the accompanying claims, and it shall be construed that all of the technical ideas included within the scope equivalent to the claims belong to the present invention.

INDUSTRIAL AVAILABILITY

According to the present invention, it is possible to manufacture an organic device having excellent device characteristics of high luminance, high light emission and long life, and thus has industrial applicability. 

1. An organic electronic element comprising a first electrode, a second electrode, and an organic material layer formed between the first electrode and the second electrode, wherein the organic material layer comprises an emitting layer, wherein the emitting layer comprises a first host compound represented by Formula 1 and a second host compound represented by Formula 2 as a phosphorescent emitting layer:

in Formula 1 and Formula 2, 1) M is a C₆-C₆₀ arylene group or a substituent represented by Formula 1-1, 2) A, B, C and D are each independently a C₆-C₆₀ aryl group or a C₂-C₆₀ heterocyclic group, and C is bonded to L³, D is bonded to L⁴, 3) X¹ is S or O, and X² and X³ are each independently N-L⁸-Ar⁸, O, S or CR′R″, wherein R′ and R″ are selected from the group consisting of hydrogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₃-C₆₀ heterocyclic group; a C₁-C₅₀ alkyl group; and -L′-N(R^(a))(R^(b)), and R′ and R″ may be bonded to each other to form a spiro, 4) x is an integer of 0˜3, y is an integer of 0˜4, 5) R^(c) and R^(d) are each independently selected from a group consisting of hydrogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R^(a))(R^(b)), wherein R^(a) and R^(b) are each independently selected from a group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₂-C₆₀ heterocyclic group including at least one hetero atom of O, N, S, Si or P; and L′ is selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic, 6) Ar¹, Ar², Ar³, Ar⁴, Ar⁵, Ar⁶, Ar⁷ and Ar⁸ are each independently selected from the group consisting of a C₆-C₆₀ aryl group; a C₂-C₆₀ heterocyclic group including at least one hetero atom of O, N, S, Si or P; a fluorenyl group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; C₆-C₃₀ arylthio group; a C₆-C₃₀ aryloxy group; and Ar¹ and Ar², or Ar⁴ and Ar⁵ may be bonded to each other to form a ring, 7) L¹, L², L³, L⁴, L⁵, L⁵, L⁶, L⁷ and L⁸ are independently selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; or a C₂-C₆₀ heteroarylene group containing at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and an aliphatic hydrocarbon group; wherein, the aryl group, fluorenyl group, arylene group, heterocyclic group, fluorenylene group, fused ring group, alkyl group, alkenyl group, alkoxy group and aryloxy group may be substituted with one or more substituents selected from the group consisting of deuterium; halogen; a silane group; siloxane group; boron group; germanium group; cyano group; nitro group; a C₁-C₂₀ alkylthio group; C₁-C₂₀ alkoxyl group; C₁-C₂₀ alkyl group; C₂-C₂₀ alkenyl group; C₂-C₂₀ alkynyl group; C₆-C₂₀ aryl group; C₆-C₂₀ aryl group substituted with deuterium; a fluorenyl group; C₂-C₂₀ heterocyclic group; C₃-C₂₀ cycloalkyl group; C₇-C₂₀ arylalkyl group and C₈-C₂₀ arylalkenyl group, wherein the substituents may be bonded to each other to form a saturated or unsaturated ring, wherein the term ‘ring’ means a C₃-C₆₀ aliphatic ring or a C₆-C₆₀ aromatic ring or a C₂-C₆₀ heterocyclic group or a fused ring formed by the combination thereof.
 2. The organic electronic element of claim 1, wherein in Formula 1, A, B, C, and D are each independently selected from the group consisting of any one of the following Formulas a-1 to a-7:

in Formulas a-1 to a-7, Z¹ to Z⁴⁸ are each independently CR^(e) or N, Z¹ to Z⁴⁸ bonded to L¹ to L⁴ are carbon (C), R^(e) is the same as the definition of R^(a) in claim 1, * indicates the position to be condensed.
 3. The organic electronic element of claim 1, wherein L¹, L², L³, L⁴, L⁵, L⁶, L⁷ and L⁸ in Formula 1 or 2 are represented by any one of the following formulas b-1 to b-13:

in Formulas b-1 to b-13, Y is N-L⁹-Ar⁹, O, S or CR′R″, L⁹ is the same as the definition of L¹ in claim 1, Ar⁹ is the same as the definition of Ar¹, in claim 1, R′ and R″ are the same as defined in claim 1, a, c, d and e are each independently an integer of 0 to 4 and b is an integer of 0 to 6, f and g are each independently an integer of 0 to 3, h is an integer of 0 to 2, i is an integer of 0 or 1, R¹, R² and R³ are each independently selected from the group consisting of hydrogen; deuterium; tritium; halogen; cyano group; nitro group; C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L^(a)-N(R^(h))(R^(i)); or in case a, b, c, d, e, f and g are 2 or more, and h is 2 or more, R¹, R² and R³ are in plural being the same or different, and a plurality of R¹ or a plurality of R² or a plurality of R³ or adjacent R¹ and R², or adjacent R² and R³ may be bonded to each other to form an aromatic or a heteroaromatic ring, wherein L^(a) is selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; a C₂-C₆₀ heterocyclic group containing at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and C₃-C₆₀ aliphatic hydrocarbon group; R^(h) and R^(i) are each independently selected from the group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group containing at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring, Z⁴⁹, Z⁵⁰, and Z⁵¹ are each independently CR^(g) or N, at least one of Z⁴⁹, Z⁵⁰, and Z⁵¹ is N, R^(g) is selected from the group consisting of hydrogen; deuterium; tritium; halogen; cyano group; nitro group; C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and adjacent R¹ and R^(g) may be bonded to each other to form an aromatic or a heteroaromatic ring.
 4. The organic electronic element of claim 1, wherein at least one of Ar¹, Ar², Ar³, Ar⁴ and Ar⁵ is represented by Formula 1-2:

in Formula 1-2, E and F are the same as the definition of A in claim 1, X⁵ is N-L¹⁰-Ar¹⁰, O, S or CR′R″, L¹⁰ and L¹¹ are the same as the definition of L¹ in claim 1, Ar¹⁰ is the same as the definition of Ar¹ in claim 1, R′ and R″ are the same as defined in claim
 1. 5. The organic electronic element of claim 1, wherein the first host compound represented by Formula 1 includes a compound represented by Formula 3:

in Formula 3, X¹, X², Ar¹, Ar², Ar³, Ar⁴ and Ar⁵ are the same as defined in claim 1, Z⁵², Z⁵³, Z⁵⁴ and Z⁵⁵ are each independently CR^(e) or N, Z⁵², Z⁵³, Z⁵⁴ or Z⁵⁵ bonded to N is carbon (C), R^(e) is the same as the definition of R^(a) in claim
 1. 6. The organic electronic element of claim 1, wherein X¹ and X² in Formula 1 are each independently O or S.
 7. The organic electronic element of claim 1, wherein the second host compound represented by Formula 2 is represented by any one of Formulas 4 to 7 below:

in Formulas 4 to 7, X², L⁵, L⁶, L⁷, Ar⁶, Ar⁷, R^(c), R^(d), x and y are the same as defined in claim
 1. 8. The organic electronic element of claim 1, wherein the second host compound represented by Formula 2 is represented by Formula 8 below:

in Formula 8, X², L⁵, L⁶, L⁷, Ar⁶, R^(c), R^(d), x and y are the same as defined in claim 1, X⁴ is the same as the definition of X², R^(e) and R^(f) are the same as the definition of R^(d) and R^(c), n is the same as the definition of y, m is the same as the definition of x.
 9. The organic electronic element of claim 1, wherein the second host compound represented by Formula 2 is represented by Formulas 9 to 12 below:

in Formulas 9 to 12, X², L⁵, L⁶, L⁷, Ar⁶, R^(c), R^(d), x and y are the same as defined in claim 1, X⁴ is the same as the definition of X², R^(e) and R^(f) are the same as the definition of R^(d) and R^(c), n is the same as the definition of y, m is the same as the definition of x.
 10. The organic electronic element of claim 1, wherein the first host compound represented by Formula 1 is any one of Compounds 1-1 to 1-265 below:


11. The organic electronic element of claim 1, wherein the second host compound represented by Formula 2 is any one of the following compounds:


12. The organic electronic element of claim 1, comprising at least one hole transport band layer between the first electrode and the emitting layer, wherein the hole transport band layer includes a hole transport layer, an emitting auxiliary layer, or both, and the hole transport band layer includes the compound represented by Formula
 1. 13. The organic electronic element of claim 1, wherein the compounds represented by Formula 1 and by Formula 2 are mixed in a ratio of any one of 1:9 to 9:1 and included in the emitting layer.
 14. The organic electronic element of claim 1, wherein the compounds represented by Formula 1 and by Formula 2 are mixed in a ratio of 1:9 to 5:5 and included in the emitting layer.
 15. The organic electronic element of claim 1, wherein the compounds represented by Formula 1 and by Formula 2 are mixed in a ratio of 2:8 or 3:7 and included in the emitting layer.
 16. An electronic device comprising: a display device including the organic electric element of claim 1; and a control unit for driving the display device.
 17. The compound of claim 16, wherein the organic electric element is at least one of an OLED, an organic solar cell, an organic photo conductor, an organic transistor and an element for monochromic or white illumination. 